X120Mn12 is called Mn13.
SHANGHAI WEIMETAL INTERNATIONAL CO.,LTD.
Grade:120Mn12 < W1.3401 - AISI A 128 (A) - GOST 110 F 13 L - JIS SCMnH 1/11>
GERMANY STEEL GRADE£º G-X120Mn12
THE ASTEM£º£Á£Ó£Ô£Í A128
EUROPE£º X120Mn12
CHINA£ºMn13
CHINA CASTING£ºZGMn13
HIGH MANGANESE STEEL PLATE,ROUND BAR,FLATE BAR WIRE AND SO ON
hot rolled plate hot round bar
CHEMICAL COMPOSITION(%)
C |
Si |
Mn |
P |
S |
Cr |
1.0~1.3 |
0.3~0.5 |
11.0~14.0 |
¡Ü0.100 |
¡Ü0.040 |
(¡Ü1.50) |
M
tensile strength Rm(Mqa) |
yield strength Re(Mpa) |
reduction of area A(%) |
ballistic work Akv(J) |
880~1130 |
¡Ý410 |
¡Ý40 |
124(normal temperature) |
X120Mn12 Nonmangic steel X120Mn12,good X120Mn12£¬better X120Mn12,Baosteel X120MN12,Tisco X120Mn12
We always have some X120Mn12 plate in stock.
X120Mn12 TISCO£º2.0MM×1000MM×2000MM
X120Mn12 TISCO£º3.0MM×1000MM×2000MM
X120Mn12 TISCO£º4.0MM×1000MM×2000MM
X120Mn12 TISCO£º5.0MM×1000MM×2000MM
X120Mn12 Baosteel£º6.0MM×2000MM×6000MM
X120Mn12 Baosteel£º8.0MM×2000MM×6000MM
X120Mn12 Baosteel£º10.0MM×2000MM×6000MM
X120Mn12 Baosteel£º12.0MM×2000MM×6000MM
X120Mn12 Baosteel£º20.0MM×2000MM×6000MM
X120Mn12 could be made a fresh order.The size as your inquire.
The widthe( 6-60mm plates) is 1500mm--2440 ,and the length is 4000-8000.
HIGH MANGANESE STEEL
STEEL GRADE£ºX120Mn12
SPECIFICTION£ºBTGC001-2015£¨BAOSTEEL£©
X120Mn12 characteristics and scope of application:
X120Mn12 magnetic impact abrasion resistance is high manganese steel.Suitable for high impact wear industry.Shot blasting machine, road machinery, special engineering, mining, metallurgy, coal, machinery, electrical, etc.
X120Mn12 is HIGH MANGANESE steel, HIGH MANGANESE STELL SCRAP) is a strong resistance to impact, pressure material abrasion resistant materials such as the best choice.The greatest characteristic of high manganese steel has two: one is the external impact, the greater the its surface wear resistance is higher;Second, as the surface hardening layer gradually wear, will continuously to form new work hardening layer.X120Mn12 copper plate to the strong impact wear and big stress wear has excellent wear resistance, in use process will not be broken, but also convenient for cutting, welding, bending, such as easy machining performance.Traditional use of highly complex cast iron wear only for mobile has good abrasion resistance.X120Mn12 rolled plate can effectively reduce the use of equipment parts cost and saving equipment maintenance cost, enhance the competitiveness of their products.
X120Mn12 chemical composition:
Carbon C: 1.00 ~ 1.30
Si Si: 0.25 ~ 0.50
Manganese Mn: 11.00 ~ 14.00
S: sulfur 0.040 or higher
P P: 0.100 or less
Chromium Cr: 1.50
X120Mn12 mechanical properties:
Tensile strength of sigma b (Mpa) : 880 ~ 1130
Yield strength Re (Mpa) : p. 410
Elongation delta (%) : 40 or higher
Shock absorption Akv (J) : 124 (room temperature)
Hardness: 229 hb or less
X120Mn12 heat treatment specification and metallographic organization:
Heat treatment specification: solid fusion processing < water toughening treatment >, 1060 ~ 1100 ¡æ, water cooling